Textile Ceramic Yarn Tensioner For Skein Winder

Textile ceramics are mainly produced from alumina ceramic materials, which have excellent comprehensive technical properties such as high mechanical strength, high hardness, low high-frequency dielectric loss, high temperature insulation resistance, chemical resistance and good thermal conductivity.

Material option:

Steatite

Alumina up to 99.7 % or 95% alumina

Titania

Zirconia

Range of products:

Flange Eyelet, Double flange eyelet, Slotted eyelet, groove eyelets, step eyelet, Cut Eyelet, Step Eyelets, Tubes, Rods, Sleeve, Ring, Bush, Disc, Dish, Washer, Plates Trap Guide, Traverse Guide, Pig tail Guide, Dog tail Guide, Rollers, Oilers, Oiling Nozzles Cutters

Application :

Yarn manufacturing machines

Twister machines

Airjet looms

Circular looms

weaving machines

winder machines

Rope,Tap plants

Customized guides as per detailed drawings and specifications.

Production process of textile ceramics:

1: Making mould

2: Prepare material according to requirement.

3: Blending material

4: Extrude items

5: Fire about 48 hours (depending on the size of the product)

6: Sanding (polishing)

7: Pick out superior products for delivery

Material data:

Item	Unit	95% al2o3	99% al2o3	Zirconia	Black Tio2	Yellow Tio2
Color		white,pink	cream,pink	white,black,yellow	Black	Yellow
Density	g/cm3	3.65	3.9	6	4	4
Flexural strength	MPA	290	390	1300	70	70
Compressive strength	MPA	3300	3900	3000	600	600
Vickers hardness	HV0.5	1800	2000	1150	900	900
Thermal expansion cofficient	10-6 K-3	5-8.3	5.4-8.3	10	8.5	8.5
Thermal conductivity	w/mk	23	28	2	25	25